Sinterizasyon prosedürünün monolitik zirkonyanýn optik özelliklerine ve dayanýmýna etkisi

GÝRÝÞ ve AMAÇ: Farklý sinterizasyon prosedürlerinin farklý kalýnlýklardaki monolitik zirkonun (MZ) optik özelliklerine etkisini inceleyen çalýþmalar sýnýrlýdýr. Bu çalýþmanýn amacý sinterizasyon prosedürü ve kalýnlýðýn MZ’nin translusensi, opalesans ve biaksiyel kýrma dayanýmýna (BKD) etkisini deðerlendirmektir.
YÖNTEM ve GEREÇLER: Disk þeklinde 40 adet örnek presinterize zirkonya bloktan kazýnmýþ ve kalýnlýklarýna göre (0,6 ve 1,2 mm) iki gruba (n=20) ayrýlmýþtýr. Her bir gruptaki numuneler standart (S) ve hýzlý (H) prosedürlere göre sinterize edilerek alt gruplara (n=10) ayrýlmýþtýr: Standart 0,6mm, standart 1,2mm, hýzlý 0,6mm, hýzlý 1,2mm. Ardýndan her bir numunenin kontrast oraný (KO) ve opalesans parametresi (OP) hesaplandý. Optik özelliklere ait veriler 2-yönlü varyans analiziyle (α=0,05), BKD verileri ayný kalýnlýk grubu içerisinde baðýmsýz örneklerde t testleri ile karþýlaþtýrýldý (α=0,05).
BULGULAR: KO ve OP üzerinde kalýnlýðýn ve sinterizasyonun etkisi istatistiksel olarak anlamlýdýr (p<0,001). Grup-1,2’nin KO (0,72±0,1; p<0,001) ve OP (3,28±0,16; p<0,001) deðerleri grup- 0,6’ya (KO=0,62±0,02; OP=3,06±0,2) göre istatistiksel olarak anlamlý derecede yüksektir. Hýzlý sinterize edilmiþ tüm örneklerin KO (0,66±0,06; p<0,001) ve OP (3,12±0,25; p<0,05)’si standart sinterize edilmiþ tüm örneklere (KO=0,68±0,05; OP=3,22±0,13) göre istatistiksel olarak anlamlý derecede düþüktür. Grup S-1,2 ile H-1,2’nin BKD deðerleri arasýnda istatistiksel olarak anlamlý bir fark yoktur (p=0,309).
TARTIÞMA ve SONUÇ: Bu çalýþmanýn sýnýrlarý içerisinde, kalýnlýðýn translüsensi üzerindeki etkisi çýplak gözle algýlanabilirken, sinterizasyon prosedürünün ektisi algýlanamaz. 0,6 mm’lik kalýnlýkta hazýrlanan MZ restorasyonlarýn standart prosedürle sinterlenmesi önerilir.

Effect of sintering procedure on optical properties and strength of monolithic zirconia

INTRODUCTION: Studies that researched the effect of different sintering procedures on the optical properties of monolithic zirconia( MZ) with different thicknesses are limited. The purpose of this in vitro study was to investigate the effects of sintering procedure and thickness on the translucency, opalescence and biaxial flexural strength (BFS) of MZ.
METHODS: Forty disc-shaped MZ specimens were milled with presinterized-zirconia blank and divided into (n=20) two groups according to thicknesses (0.6 and 1.2mm). Each groups was sintered according to two different (standard [S] and fast [F]) sintering procedures then divided into two subgroups (n=10): Standart 0.6 mm, standart 1.2 mm, fast 0.6 mm, fast 1,2 mm. After that, contrast ratio (CR) and opalescence parameter (OP) were calculated. Data of optical parameters were analyzed with two-way analysis of variances (α=.05). The data of strength were analyzed by independent sample t-tests within the same thickness groups (α=.05).
RESULTS: The effect of thickness and sintering on CR and OP was statistically significant (p<.001). CR (0.72±0.1; p<.001) and OP (3.28±0.16; p<.001) values of group-1.2 were statistically significantly higher than group-0.6 (CR=0.62±0.02; OP=3.06±0.2). CR (0.66±0.06; p<.001) and OP (3.12±0.25; p<.05) values of all fast sintered samples were statistically significantly lower than all standard sintered samples (CR=0.68±0.05; OP=3.22±0.13). There was no statistically significant difference between BFS values of Group S-1.2 and F-1.2 (p=.309).
DISCUSSION AND CONCLUSION: The effect of the thickness on the translucency is perceivable by the naked-eye, while the effect of the sintering procedure is not. It is recommended to MZ restorations with 0.6 mm are sintered by standard procedure.